Bergamid™ A70 GK30 H NC132
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 948Y6N_Bergamid-A70-GK30-H-NC132.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass beads reinforced PA66 compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.90 - 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 85.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 4500 | MPa | ASTM D790 |
| Flexural Strength 3 | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 80.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M20GHPPCC | McCann Plastics Inc. | PP Homopolymer | McCann PP |
| AKROTEK® PEEK GF 50 9 natural (5183) | AKRO-PLASTIC GmbH | PEEK | AKROTEK® |
| Gallonprene® GP310-7003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ICORENE® N4450 | ICO Polymers EMEA, A Division of A. Schulman | PP Homopolymer | ICORENE® |
| Karina CLEAR PVC COMPOUND -E 80/274-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |