Nypol® PA A3 T30 N1 NTLA014 NR453
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8u2k98_Nypol-PA-A3-T30-N1-NTLA014-NR453.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural with 30% mineral reinforced, with graphite additive, lubricated, good resistance to wear and good set of thermal properties, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.34 to 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (2.00 mm) | 0.20 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.2 | -- | % | |
| Saturation | 7.5 | -- | % | |
| Ash Content | 28 to 32 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 85.0 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | 8.0 | % | ASTM D638 |
| Flexural Modulus | 6000 | 2600 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 11 | 9.0 | kJ/m² | |
| 23°C | 18 | 32 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | |||
| -30°C | -- | 8.00 | kJ/m² | |
| 23°C | 15.0 10.0 | 31.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 240 | -- | °C | |
| 1.8 MPa, Unannealed | 209 | -- | °C | |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 250 to 275 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Clear G 120 Rnew | Arkema | Nylon, Unspecified | Rilsan® Clear |
| SEMICOSIL® 992JC | Wacker Chemie AG | Silicone | SEMICOSIL® |
| Hylon® N1040MGHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| INELEC PA12CF20 | Infinity LTL Engineered Compounds | Nylon 12 | INELEC |
| Lytex 4149 | Quantum Composites Inc. | Epoxy | Lytex |