ALCUDIA® LDPE CA-2130A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8R4ZqX_ALCUDIA-LDPE-CA-2130A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® CA-2130A is stabilized with HALS (colourless) and antioxidants. This compound offers high solar radiation resistance. APPLICATIONS Films for greenhouses and tunnels cover. ALCUDIA® CA-2130A, 180 µm thickness films have a lifetime of two continuous agricultural seasons (two winters and one summer) in geographical areas where maximum solar radiation is 160 kLy. For further information, contact to Technical Assistance and Development Department or Commercial Attention Service. Recommended melt temperature range from 190 to 210°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 180 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Fracture, 180 µm, blown film | 19.0 | MPa | ISO 527-3 |
| TD : Fracture, 180 µm, blown film | 19.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 180 µm, blown film | 500 | % | ISO 527-3 |
| TD : Fracture, 180 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (180 µm, blown film) | 750 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 180 µm, blown film | 6.0 | N | ISO 6383-2 |
| TD : 180 µm, blown film | 9.0 | N | ISO 6383-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (180 µm, blown film) | 40 | % | ASTM D1003 |
| Global Transmission of Visible Light 1(180.0 µm) | 90 | % | EN 13206 |
| Additional Information |
|---|
| Data taken from 180 µm thickness film, blown up ratio 2.25:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Smooth-Cast® 60D | Smooth-On, Inc | PUR, Unspecified | Smooth-Cast® |
| Tisoplen® PPC 10 MNF CALCITE | Tisan | PP Copolymer | Tisoplen® |
| Durethan® BKV 25 FN01 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Ekalon® 20 E II S | Sattler KunststoffWerk GmbH | PC | Ekalon® |
| Karina IVORY PVC COMPOUND 70900-35/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |