Zytel® MT409AHS BK010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8OLCSu_Zytel-MT409AHS-BK010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughened, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.7 | -- | % | |
| Flow | 1.7 | -- | % | |
| Water Absorption (24 hr) | 0.90 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1080 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 60.0 | 42.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | 27 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 28 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2200 | 1080 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 12 | -- | kJ/m² | |
| 23°C | 19 | -- | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 11 | -- | kJ/m² | |
| -30°C | 13 | -- | kJ/m² | |
| 23°C | 17 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 187 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-4 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 4.7E+11 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 9.7E+11 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.90 | 9.80 | ||
| 1 MHz | 3.70 | 4.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 6.0E-3 | 0.44 | ||
| 1 MHz | 0.013 | 0.51 | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 29 | -- | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecodur® PB70 GR15 NL100 | Eurotec Engineering Plastics | PBT | Tecodur® |
| Nycal™ 2120H Bk-7 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Evoprene™ 3273 | AlphaGary | SBS | Evoprene™ |
| INEOS PP 101-ZB25 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| LNP™ LUBRILOY™ D20009 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |