SCHULAMID® 66 MNF 2510 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H84s6Q_SCHULAMID-66-MNF-2510-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% mineral and glass fiber reinforced, heat stabilized Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8100 | 5000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 125 | 70.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | 7.0 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 40 | 55 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 238 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | > 250 | -- | °C | ISO 306/A50 |
| -- | 245 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2501TH00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| BESTNYL SE25VI01AX-1 | Triesa Plastics | Nylon 66 | BESTNYL |
| G-Blend 85 HI PC/ABS | Gardiner Compounds Ltd. | PC+ABS | G-Blend |
| Escorene™ Ultra FL 00714 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Plaslube® PA6/6 GF43 ML2 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |