PureTherm® 1001C Aluminum Look Alike

Category:	Film, PVC , PVC Film
Manufacturer:	Tekni-Films, a div of Tekni-Plex
Trademark:	PureTherm®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7eufHW_PureTherm-1001C-Aluminum-Look-Alike.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PureTherm® 1001C Aluminum Look Alike is a rigid PVC film with transmission values below the USP standard of 10% in the critical ultraviolet 290 — 450 nm range.

This film is the same as PureTherm® 1001C with the addition of white pigment to allow for the packaging of light sensitive pharmaceutical products or where it is desirable that the blister contents are not visible.

Applications for PureTherm® 1001C include blister packaging of tablets, capsules, lozenges, suppositories as well as use in laminations.

General Information
Additive	Pigment
Features	High Rigidity Self Extinguishing
Uses	Laminates Pharmaceutical Packaging
Appearance	Aluminum Opaque
Forms	Film

Physical	Nominal Value	Unit
Specific Gravity	1.33	g/cm³

Films	Nominal Value	Unit	Test Method
Film Thickness ¹	127 to 1020	µm

Thermal	Nominal Value	Unit	Test Method
Cold Impact	Good
Heat Distortion	75	°C	ASTM D1637

Additional Information	Nominal Value	Unit
Roll Width ²	< 106.70	cm
Thermoforming Molding Temperature	100 to 175	°C

Films	Nominal Value	Unit	Test Method
Tensile Strength - MD (Yield)	48.0	MPa	ASTM D882
Oxygen Transmission Rate (Wet) (23°C, 250 µm, 100% RH)	18.1	cm³/m²/24 hr	ASTM F1927
Water Vapor Transmission ³	3.1	g/m²/24 hr	ASTM E96
Free Shrinkage	-4.0 to 4.0	%	ASTM D2732

Note Message
1 .	Thickness tolerance: ±10%
2 .	Roll width tolerance: ±1.5 mm
3 .	at 10 mil at 38°C, 90% RH

Resin Grade	Manufacturer	Category	Trademark
Viton® B-910	DuPont Performance Elastomers	Fluorelastomer	Viton®
COPEC® CC8OCN (Series: VS/AD1)	KRAIBURG TPE	TPE	COPEC®
Flontech® FT-GL5-M5-6	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
Dyna-Purge® C	Dyna-Purge, division of Shuman Plastics	Proprietary	Dyna-Purge®
LNP™ THERMOTUF™ R1000I compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOTUF™