Baytec® SPR-256D
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7cTPBg_Baytec-SPR-256D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec SPR-256D is a two-component, 100%-solids spray system with a Shore hardness of 56D. The isocyanate component is a modified diphenylmethane diisocyanate (MDI) prepolymer, and the polyol component is a polyether polyol blend. Baytec SPR-256D spray system is typically used for in-mold spray applications with polyurethane structural composites. As with any product, use of Baytec SPR-256D in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 56 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 16.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 54 | % | ASTM D638 |
| Elongation- Humid Aging 1 | 64 | % | |
| Tensile Strain at Yield 2 | 10.3 | MPa | |
| Tensile Strength 3 | 15.2 | MPa |
| Thermal | Nominal Value | Test Method | |
|---|---|---|---|
| Cold Resistance | No Cracking | SAE J323 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging | 98 | % | GM 9305P |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 166 | mg | ASTM D3489 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | |||
| -- 4 | 56.6 | kN/m | ASTM D624 |
| Cracking | 13 | kN/m | ASTM D1938 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 110, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Clear amber liquid Specific Gravity @ 25°C: 1.14 Viscosity @25°C: 600 mPa Flash Point, PMCC: 210°C NCO: 19 wt% Part B Type: Polyol Appearance: Gray opaque liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 1500 mPa-s Flash Point, PMCC: 201°C Hydroxyl Number: 233 mg KOH/g Processing Temperature: 19 to 66°CGel Time: 5 to 15 secTack-Free: 30 sec |
| Note Message | |
|---|---|
| 1 . | GM 7001, K9588 |
| 2 . | 5 hours at 120°C, 100% RH, GM 7001, X9588 |
| 3 . | 21 days at 120°C, GM 7001M, W6655 |
| 4 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® SB9304 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| ELASTOSIL® LR 3040/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Plantic® WR700 | Plantic Technologies Limited | Biodeg Polymers | Plantic® |
| PLUSTEK PA303G43 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Sylvin 4280-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |