InnoTuf® TP-4015
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6KNaLz_InnoTuf-TP-4015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TP-4015 is an impact resistant polyurea formulated for vacuum assisted casting systems and short mold cycle times. Excellent physical properties can be obtained without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.22 | g/cm³ | |
| Hardener | 1.22 | g/cm³ | |
| Base Resin | 1.22 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1080 | MPa | ASTM D790 |
| Flexural Strength | 51.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 116 | °C | |
| 1.8 MPa, Unannealed | 95.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 50 Mix Ratio by Weight: 50 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 30 to 50 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.20 | Pa·s | |
| 38°C 2 | 0.35 | Pa·s | |
| 38°C 3 | 0.70 | Pa·s | |
| Curing Time 4 | 88 | hr | |
| Gel Time | 1.4 to 1.6 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Modulus | 927 | MPa | |
| Tensile Strength | 42.7 | MPa | ASTM D638 |
| Tensile Elongation at Break | 11 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 16 hours at 150°F + 3 days at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONACOM PS 5370 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |
| TOTAL Polypropylene PPC 4944CWZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| BorLite™ OPE792 | Borealis AG | LLDPE | BorLite™ |
| Polifor® QD 813 Y001 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| Sylvin 9940-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |