ULTEM™ 2310R resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u3SgVh_ULTEM2310Rresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. UL94 V0 and 5VA listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 - 0.40 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.18 | % | ASTM D570 |
| Saturated, 23°C | 0.90 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 165 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 165 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8500 | MPa | ISO 178 |
| Flexural Stress | 225 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 20.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| -30°C 4 | 40 | kJ/m² | ISO 180/1U |
| 23°C 5 | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, unannealed, 100 mm span | 215 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 210 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 228 | °C | ASTM D1525 7 |
| -- | 225 | °C | ISO 306/A50 |
| -- | 213 | °C | ISO 306/B50 |
| -- | 220 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.30 | W/m/K | ISO 8302 |
| RTI Elec | 180 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 180 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 26 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.40 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.6E-3 | IEC 60250 | |
| 60 Hz | 1.6E-3 | IEC 60250 | |
| 1 kHz | 1.5E-3 | IEC 60250 | |
| 1 MHz | 2.3E-3 | IEC 60250 | |
| 2.45 GHz | 5.3E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.250 mm | V-0 | UL 94 | |
| 1.20 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 48 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 350 - 400 | °C | |
| Middle Temperature | 360 - 410 | °C | |
| Front Temperature | 370 - 420 | °C | |
| Nozzle Temperature | 360 - 410 | °C | |
| Processing (Melt) Temp | 370 - 410 | °C | |
| Mold Temperature | 140 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 120*10*4 mm |
| 7 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 1415L (YC37F) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Generic TPEE | Generic | TPEE | Generic |
| ESTADIENE 1016 HT V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| LNP™ STAT-KON™ PX09011 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |
| Lucent PEI PEI-100 | Lucent Polymers, Inc. | PEI | Lucent PEI |