Maxxam™ PP5930 Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6GTxyP_Maxxam-PP5930-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 34 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7400 | MPa | ISO 527-2 |
| Tensile Stress 1(Yield) | 96.0 | MPa | ISO 527 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 8.5 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 185 to 200 | °C | |
| Middle Temperature | 195 to 215 | °C | |
| Front Temperature | 195 to 220 | °C | |
| Nozzle Temperature | 200 to 215 | °C | |
| Mold Temperature | 40.0 | °C | |
| Back Pressure | 80.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hapflex™ 781 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Hifax TYC 2005P S62840 | LyondellBasell Industries | PP Copolymer | Hifax |
| Starex WX-9130 | LOTTE ADVANCED MATERIALS CO., LTD. | ASA | Starex |
| POCAN® B 4235 Z 000000 | LANXESS Corporation | PBT | POCAN® |
| LNP™ STAT-KON™ RE006 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |