Resirene READ 9400 RAF
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Resirene, S.A. de C.V. |
| Trademark: | Resirene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 61bp7L_Resirene-READ-9400-RAF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resirene READ 9400 RAF is an easy to process HIPS and is optimal for injection molding process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1790 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 14.0 | MPa | |
| Break | 10.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 1.0 | % | |
| Break | 35 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 120 | J/m | ASTM D256 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | < 240 | °C | |
| Mold Temperature | 38.0 to 82.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC6HBZ (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Toyolac® 855VG20 | Toray Resin Company | ABS | Toyolac® |
| ASI POLYPROPYLENE 3479-01 | A. Schulman Inc. | PP Random Copolymer | ASI POLYPROPYLENE |
| LEXAN™ ML104R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| LEXAN™ XHT2141 resin | SABIC Innovative Plastics | PC | LEXAN™ |