TOTAL Polystyrene Crystal 1050T
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5o68Vf_TOTALPolystyreneCrystal1050T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL TransmYrene POLYSTYRENE 1050T is a high heat resistant, high transmittance crystal polystyrene designed for optical applications. This distinctive grade is specially produced to maximize the light going through it and consequently improving its optical properties. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.2 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.040 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 43.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 2950 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact Strength | 8.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ISO 306/A50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Dielectric Strength | 150 | kV/mm |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (3060 µm) | 0.45 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | < 240 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 | °C | |
| Drying Time | 2.0 | hr | |
| Melt Temperature | < 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 F TFE 13 SI 2 | RTP Company | Nylon 12 | RTP |
| RapidVac™ VA-254 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Texalan® 7 Series 785A | Austin Novel Materials Co. Ltd. | TPU Alloy | Texalan® 7 Series |
| Eastar™ CN015 Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Echo® RPEHDW NAT (Injection) | Ravago Manufacturing Americas, LLC | HDPE | Echo® |