Order Products : sales@su-jiao.com
KEBATER® PBT BF115
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BARLOG plastics GmbH |
| Trademark: | KEBATER® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5DCrWc_KEBATER-PBT-BF115.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 15% glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 4.0E-5 | cm/cm/°C | |
| Transverse | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+19 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.60 mm) | HB | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8808-70D Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |
| Wanthane® WHT-1195 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Gallonprene® GP410-6001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Capilene® TP 75 AV | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Styropek® BF 395M | Styropek S.A. de C.V. | PS (EPS) | Styropek® |