G-Lex F55HM0003
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Gas Authority of India Limited |
| Trademark: | G-Lex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 57wGeN_G-Lex-F55HM0003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
G-Lex F55HM0003 is a high density (HMW) polyethylene material,. This product is available in the Asia-Pacific region, and the processing method is: film extrusion. The main features of the G-Lex F55HM0003 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 9.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With itself-dynamic, blown film | 0.21 | ASTM D1894 | |
| With itself-static, blown film | 0.22 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 15 µm, blown film | 49.0 | MPa | ASTM D882 |
| TD : Broken, 15 µm, blown film | 41.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 15 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 15 µm, blown film | 600 | % | ASTM D882 |
| Dart Drop Impact (15 µm, Blown Film) | 110 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15 µm, blown film | 45 | g | ASTM D1922 |
| TD : 15 µm, blown film | 140 | g | ASTM D1922 |
| Additional Information |
|---|
| Data gathered from 15 µ blown film with a BUR of 4:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RMA 113/113F | Ronald Mark Associates, Inc. | PVC Copolymer | RMA |
| Shandong PA1212 Special Resin for Badminton | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Tekulon FR 645 | TEKUMA Kunststoff GmbH | PC | Tekulon |
| Torayca® 2701T-30V | Toray Resin Company | Nylon 610 | Torayca® |
| LNP™ THERMOCOMP™ 5C003 compound | SABIC Innovative Plastics | PVDF | LNP™ THERMOCOMP™ |