Latimass 37 B01-01 D025
| Category: | PLA , Polylactic Acid |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latimass |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Kagzv_Latimass-37-B01-01-D025.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Specific density compound based on Bio-Polymer (PLA, PHB, ...). Special filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.20 to 0.60 | % | |
| Flow : 2.00 mm | 0.20 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.50 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 55.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 60.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 to 50.0 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 15.0 to 30.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V973 NAT601UV AF | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Matrixx FP63E23 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| VAMPSTAT Y 00U 06 V0 26 SC2 ST | Vamp Tech | Nylon 66 | VAMPSTAT |
| NYCOA Polyamide 1047 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| China PPS hGR40 DL/hGR41 DL | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |