TRANSMARE® 14CT30-0.002
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 51f1lL_TRANSMARE-14CT30-0-002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 14CT30-0.002 is a 30% standard (gray) talc filled polypropylene copolymer for injection molding purposes with high impact and good flow. Not suitable for light colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 10 | g/10 min | |
| 230°C/5.0 kg | 50 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 20.0 | MPa | |
| Break, 4.00 mm | 17.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 2.5 | % | |
| Break, 4.00 mm | 30 | % | |
| Flexural Modulus 1 | 2750 | MPa | ISO 178 |
| Flexural Stress 2 | 34.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C | 2.0 | kJ/m² | |
| -20°C | 2.5 | kJ/m² | |
| 0°C | 3.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 2.5 | kJ/m² | |
| -20°C | 3.2 | kJ/m² | |
| 0°C | 4.3 | kJ/m² | |
| 23°C | 13 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 143 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DENYL 6 3010 | Vamp Tech | Nylon 6 | DENYL |
| EnCom GF15 PPE-PS | EnCom, Inc. | PPE+PS | EnCom |
| HIPOLEN P® TA 41 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| Karina CLEAR PVC COMPOUND 105801/201-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® AKV 50 H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |