COSMOPLENE® AW191
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4fobGm_COSMOPLENE-AW191.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE AW191 is high impact PP copolymer manufactured by gas phase process technology licensed from Sumitomo Chemical Co. Japan. COSMOPLENE AW191 is medium flow, super high impact copolymer grade. COSMOPLENE AW191 is specially designed for industrial use such as crates, bumper, automotive parts etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 1.4 | % | |
| Across Flow : 2.00 mm | 1.4 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 68 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 20.0 | MPa | |
| Break | 22.5 | MPa | |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Flexural Modulus | 870 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 80 | J/m | |
| 23°C | 550 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 190 to 230 | °C | |
| Front Temperature | 190 to 230 | °C | |
| Injection Pressure | 6.86 | MPa | |
| Clamp Tonnage | 0.98 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN TR-935 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| 4MID® 9B22230 H | 4Plas | Nylon 6 | 4MID® |
| Alpha PE GPE 2001-R NATURAL | AlphaGary | PE, Unspecified | Alpha PE |
| Amilan® CM3006 | Toray Resin Company | Nylon 66 | Amilan® |
| LNP™ THERMOCOMP™ RF006XXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |