CONTINUUM™ DGDC-2480 BK
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CONTINUUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4FFN73_CONTINUUM-DGDC-2480-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CONTINUUM™ DGDC-2480 BK Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long-term hydrostatic strength combined with outstanding resistance to slow crack growth and rapid crack propagation are desired. Suitable applications include natural gas distribution pipes, industrial piping, mining, sewage, and municipal water service lines. Industrial Standards Compliance:
NOTES: (1) The first five numbers of the cell classification are based on natural resin. The last number and letter are based on black resin (natural resin plus 6.5% DFNF-0092). |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| Natural | 0.949 | g/cm³ | |
| Black 1 | 0.959 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 8.5 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | > 24.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790B |
| Resistance to Rapid Crack Propagation, Pc 4 | |||
| Calculated, Full Scale : 0°C | > 46.0 | bar | ISO 13478 |
| S-4 : 0°C | > 12.0 | bar | ISO 13477 |
| Resistance to Rapid Crack Propagation, Tc - S-4 @ 10 bar 5 | < -17 | °C | ISO 13477 |
| Slow Crack Growth PENT 6 | > 5000 | hr | ASTM F1473 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability | > 220 | °C | ASTM D3350 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 7(23°C) | 490 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 8 | < -75.0 | °C | ASTM D746A |
| Note Message | |
|---|---|
| 1 . | Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 (6.5%). |
| 2 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 3 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 4 . | Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Dimension Ratio (SDR) 11. |
| 5 . | Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Dimension Ratio (SDR) 11. |
| 6 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 7 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 8 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 131 Z | RTP Company | PP Homopolymer | RTP |
| RR Advantage ABS 5 Black | Resin Resource, Inc. | ABS | RR Advantage |
| Softell CA 7413 A | LyondellBasell Industries | TPO (POE) | Softell |
| XANTAR® 27 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| ESPRENE EPDM 5754 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |