Order Products : sales@su-jiao.com
Genestar™ GA2330
| Category: | Nylon 9T , Polyamide 9T |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | Genestar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3xycUG_Genestar-GA2330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| For applications requiring high abrasion and heat resistance, as well as flame retardancy, such as internal gear of copying machine, GA2330 can be used. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (320°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 1.00 mm | 0.10 | % | |
| Across Flow : 1.00 mm | 0.60 | % | |
| Water Absorption 1(Equilibrium, 40°C, 95%RH) | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 175 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 197 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 285 | °C | ASTM D648 |
| Glass Transition Temperature | 125 | °C | |
| Melting Temperature | 306 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (10.0 GHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (10.0 GHz) | 0.010 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 2(320°C, 500.0 µm) | 4.90 | cm | |
| Weld Elongation | 0.40 | % | ASTM D638 |
| Weld Strength | 37.0 | MPa | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | 750kgf |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FTP 3130 | A. Schulman Inc. | TPO | POLYFORT® |
| RTP 204 GB FR | RTP Company | Nylon 66 | RTP |
| RheTech Polypropylene GC40P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Hypel® PEHD30/.950 | Entec Polymers | HDPE | Hypel® |
| LNP™ LUBRILOY™ K2000XXH compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRILOY™ |