Safrene® M 5010NAT100
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Safripol (PTY) LTD |
| Trademark: | Safrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3sSG0X_Safrene-M-5010NAT100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Safrene™ M 5010NAT100 High Density Polyethylene Resin is a high molecular mass grade developed for pressure pipe applications. It has good impact strength, abrasion and chemical resistance properties. Safrene™ M 5010NAT100 High Density Polyethylene Resin is a suitable for small and large diameter pressure pipe applications. It is also recommended for sheet extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 9.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.25 | g/10 min | ISO 1133 |
| Viscosity Number (Reduced Viscosity) | 340.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, molding | 24.0 | MPa | ISO 527-2/50 |
| Fracture, molding | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2/50 |
| Flexural Stress (3.5% Strain, Compression Molded) | 19.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C, molded | 4.0 | kJ/m² | ISO 179 |
| 23°C, molded | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 67.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 130 - 133 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 190 - 220 | °C | |
| Cylinder Zone 3 Temp. | 190 - 210 | °C | |
| Melt Temperature | 190 - 220 | °C |
| Extrusion instructions |
|---|
| Feed Zone: 160 to 170°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1480 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Tenac™ LA543 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Sinvicomp SSZ7209 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Fainplast PVC PK 8725 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Durethan® BKV 215 H2.0 DUS035 900051 | LANXESS GmbH | Nylon 6 | Durethan® |