Alkathene® Ultra LDJ225
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3id2Nt_Alkathene-Ultra-LDJ225.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDJ225 is a low density polyethylene designed for use in the production of low gauge (20-50µm), high quality film. LDJ225 is formulated with a process stabilisation and antiblock additive package and contains other additives designed to confer very high levels of slip. LDJ225 is intended primarily for use in bread bag film and is also suitable for use in a variety of general purpose low gauge (20-50µm) film applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 32 µm, blown film | 160 | MPa | ASTM D882 |
| 2% secant, TD : 32 µm, blown film | 190 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 32 µm, blown film | 23.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 16.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 290 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 720 | % | ASTM D882 |
| Dart Drop Impact (32 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 410 | g | ASTM D1922 |
| TD : 32 µm, blown film | 180 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 32.0 µm, blown film) | 69 | ASTM D2457 | |
| Haze (32.0 µm, blown film) | 8.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V944 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sinpolene MBB2801 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Sup-tech A9705 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
| LEXAN™ CFR5630 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 5145-75 Red 6193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |