Maxxam™ TR-818.G001-8081
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tfiBFu_Maxxam-TR-818-G001-8081.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Talc reinforced polypropylene, heat and UV stabilized grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.70 - 1.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 29.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2070 | MPa | ASTM D790 |
| Flexural Strength 3 | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 32.0mm, injection molding) | 81 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Annealed, 3.20 mm) | 135 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® HP 0400 | Plastic Solutions, Inc. | PP Homopolymer | PrimaFlex® |
| FRAGOM PR/800 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| KOPA® KN3311BLK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Karina CLEAR PVC COMPOUND -E 75/316-IS-RG (GLASS CLEAR) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLEXIGLAS® Film 0F032 matt | Evonik Industries AG | Film, PMMA | PLEXIGLAS® Film |