NEMCON H PPS DP148
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | NEMCON H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3eWzWP_NEMCON-H-PPS-DP148.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPS based, thermally conducting, electrically insulating grade with improved processability. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.89 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 4500 | MPa | ASTM D638 |
| Tensile Strength 2(Break, 23°C) | 53.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C) | 2.1 | % | ASTM D638 |
| Flexural Modulus 4(23°C, 50.0 mm Span) | 4700 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 23°C, 50.0 mm Span) | 87.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 to 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | Internal Method | ||
| 23°C 6 | 0.80 to 1.1 | W/m/K | |
| 23°C 7 | 3.2 to 5.0 | W/m/K |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 300 to 330 | °C | |
| Nozzle Temperature | 310 to 340 | °C | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 140 to 160 | °C | |
| Back Pressure | 0.207 to 0.552 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Through Plane |
| 7 . | In Plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SV954 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| Propafilm™ RB120 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| tefabloc® TP SD 333 75A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Chemiton TGB2NA 30 | Franplast S.r.l. | SEBS | Chemiton |
| Karina CLEAR PVC COMPOUND -E 80/205-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |