LNP™ LUBRICOMP™ RCP36 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Qv0AC_LNP-LUBRICOMP-RCP36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RCL-4536 Product reorder name: RCP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.43 | % | ISO 294-4 |
| Flow : 24 hr | 0.15 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.93 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 29500 | MPa | ASTM D638 |
| -- | 23100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 201 | MPa | ASTM D638 |
| Break | 228 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.4 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 16400 | MPa | ASTM D790 |
| -- | 21300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 333 | MPa | ASTM D790 |
| -- | 354 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.23 | ||
| Wear Factor - Washer | 6.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 950 | J/m | ASTM D4812 |
| 23°C 3 | 65 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.90 | J | ASTM D3763 |
| -- | 2.85 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 254 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 244 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 245 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Technother® A-SV30-T | Poly Plastic | PBT | Technother® |
| Sylvin 86012-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Geon™ Vinyl Flexible 90055 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| PENTAMID AB L5 H natur | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| Sylvin 8260-90UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |