SABIC® PPcompound 19T1040
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3OGaWG_SABIC-PPcompound-19T1040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 19T1040 is a 40% talc-filled polypropylene homopolymer. The materials high fill grade makes for a very high stiffness. This combined with the high flow and good thermal stabilization makes it especially suited for complex injection molded applications requiring a very high modulus and high thermal stability. SABIC® PPcompound 19T1040 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 30.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 24.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 11 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 3600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 6.0 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 1.5 | kJ/m² | |
| 0°C, Injection Molded | 1.6 | kJ/m² | |
| 23°C, Injection Molded | 2.8 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 130 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 150 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 4.5E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 37G307 - 7809 | AD majoris | PBT | MALAT |
| Network Polymers PS CPS 80 0800 | Network Polymers, Inc. | PS (GPPS) | Network Polymers PS |
| GLS PP YN06 HF2 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| PAmpellonne® rgr_wss | Politem Plastik Ltd. | Nylon 66 | PAmpellonne® |
| SQUARE® LIM1960-60AEX/BEX | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |