Sindustris PC SC3155
| Category: | PC , Polycarbonate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3NVUry_Sindustris-PC-SC3155.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PC SC3155 is a Polycarbonate (PC) material filled with 15% glass fiber. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC SC3155 are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, 3.20 mm) | 25 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3040 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 137 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 280 to 295 | °C | |
| Middle Temperature | 285 to 300 | °C | |
| Front Temperature | 290 to 305 | °C | |
| Nozzle Temperature | 290 to 305 | °C | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 90.0 to 110 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1399 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| NEXUS Reprocessed PPH 30 RBK G33 | Nexus Resin Group, LLC. | PP Homopolymer | NEXUS Reprocessed |
| Clearflex® H&T CHH G0 | Versalis S.p.A. | VLDPE | Clearflex® H&T |
| Devcon Wear Guard™ High Load | Devcon | Epoxy | Devcon |
| Geon™ Vinyl Flexible B9000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |