DOWLEX™ 2636G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Gi54R_DOWLEX-2636G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2636G Polyethylene Resin is a cast film extrusion grade suitable for high stiffness film applications. Linear low density Polyethylene/Hexene copolymer. Improved thermal stability for high stiffness film applications. Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.933 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Puncture Force | 36.0 | N | Internal method |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 41.0 | MPa | ASTM D882 |
| TD : Fracture | 37.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 600 | % | ASTM D882 |
| TD : Fracture | 840 | % | ASTM D882 |
| Dart Drop Impact | 65 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 98 | g | ASTM D1922 |
| TD | 430 | g | ASTM D1922 |
| Tensile Energy | ASTM D882 | ||
| MD | 5.6 | J | ASTM D882 |
| TD | 7.5 | J | ASTM D882 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 90 | ASTM D2457 | |
| Haze | 3.6 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: Monolayer cast film produced on 5 layer (A/B/B/B/A) cast line. Screw Size A: 51mm; 30:1 L/D Screw Size B: 63.5mm; 30:1 L/D Die Gap: 0.6 mm Chill Roll Temperature: 21°C Melt Temperature: 274°C Line Speed: 106m/min Output: 150Kg/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 M30 | NUREL, S.A. | Nylon 6 | Promyde® |
| TECHNYL® C 52G3 MZ25 GREY R7035 CF | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| MARPOL® LL8F 805 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| EPAMOULD 660A26 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| EPALINE 386A55 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPALINE |