Zytel® PLUS PLS95G50DH2 BK261
| Category: | Nylon, Unspecified , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® PLUS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2uYLqg_Zytel-PLUS-PLS95G50DH2-BK261.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% Glass Reinforced, Heat Stabilized, Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.59 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 1.3 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16900 | 12300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 247 | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.6 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 15700 | -- | MPa | ISO 178 |
| Flexural Stress | 374 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 18 | -- | kJ/m² | |
| 23°C | 16 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 85 | kJ/m² | |
| 23°C | 95 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 263 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 254 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 265 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-5 | -- | cm/cm/°C | |
| Transverse | 8.5E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN3611SN | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| MARPOL® LDC 770 | Marco Polo International, Inc. | LDPE | MARPOL® |
| DiaAlloy FC-30 | Mitsubishi Rayon America Inc. | PC | DiaAlloy |
| Hostacom T20H563 0907 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LNP™ LUBRICOMP™ RKN14 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |