LNP™ STAT-KON™ OE008A compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2g3Gax_LNPSTATKONOE008Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* OE008A is a compound based on PPS - Branched resin containing 40% Carbon Fiber. Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound EMI-X OC-1008 Product reorder name: OE008A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.10 - 0.30 | % | Internal method |
| Transverse flow : 3.20mm | 0.60 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 181 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.90 | % | ASTM D638 |
| Flexural Modulus | 27200 | MPa | ASTM D790 |
| Flexural Strength | 263 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 480 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 AR 15 TFE 13 SI 2 | RTP Company | Nylon 66 | RTP |
| Andur AL 90 AP/Curene® 89 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Karina BLACK COLOR CONCENTRATE 48/1-FC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND 700-35/ 1-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ GF006 compound | SABIC Innovative Plastics | PSU | LNP™ THERMOCOMP™ |