ExxonMobil™ LLDPE LL 5100.09
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tQMSmt_ExxonMobil-LLDPE-LL-5100-09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ExxonMobil LL 5100.09 is a linear low density polyethylene resin with good processability and simple mixing. The particle morphology of LL 5100.09 enables it to be effectively mixed with colorants, opening agents and slip agents. |
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 14.5 | MPa | ASTM D638 |
| Fracture | 7.43 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 57 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 430 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermec™ 4301R35H | Technical Polymers, LLC | PPA | Thermec™ |
| NuSil MED-4159 | NuSil Technology | Silicone | NuSil |
| FERREX® GPP20CN46UL WHITE | Ferro Corporation | PP Homopolymer | FERREX® |
| PERLER® O07N0001B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| POCAN® KU 1-7625 901510 | LANXESS Asia/Pacific | PC+PBT | POCAN® |