Infino HI-1001B
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1GsYXb_Infino-HI-1001B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HI-1001B is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.31 to 0.38 | % | |
| Across Flow : 3.20 mm | 0.36 to 0.43 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 115 | ASTM D785 | |
| R-Scale | 107 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 61.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 48.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 55 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2500 | MPa | ASTM D790 |
| -- 6 | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 83.0 | MPa | ASTM D790 |
| -- 8 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 37 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 440 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 330 | J/m | ASTM D256 |
| 23°C 10 | 53 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 117 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 115 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 96.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 103 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 111 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 100 | °C | |
| Desiccant Dryer | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 93.2 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarFlex P 7350-9000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | Starflex |
| Gallonprene® GP520-9004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Generic ETFE | Generic | ETFE | Generic |
| Ecomass® 1700CO94 | Ecomass Technologies | Nylon 12 | Ecomass® |
| MAJORIS BG100 | AD majoris | PP, Unspecified | MAJORIS |