Pyramid™ PEEK KD2000 Compression Molded Shape
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Pyramid™ PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1BinGU_Pyramid-PEEK-KD2000-Compression-Molded-Shape.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyetheretherketone (PEEK) Tube |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus (143°C) | 3100 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648 |
| Melting Temperature | 340 | °C | DSC |
| CLTE - Flow | 4.7E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | 38 | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PS 3124 90/05 | MBA Polymers | PS (GPPS) | MBA PS |
| TECHNO ABS 545 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Sinvicomp SGH6040 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| CERTENE™ 9814 Black | Muehlstein | PP, Unspecified | CERTENE™ |
| Hostalen PP H5416 K | LyondellBasell Industries | PP Random Copolymer | Hostalen |