Ultradur® S 4090 G6

Category:	PBT+ASA , Polybutylene Terephthalate + ASA
Manufacturer:	BASF Corporation
Trademark:	Ultradur®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0hq1ma_Ultradur-S-4090-G6.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Ultradur S 4090 G6 is a 30% glass reinforced PBT+ASA blend. It produces moldings with good surface finish,is resistant to chemicals and stress cracking, and has low shrinkage and warpage. Applications Applications include highly stressed equipment housings in the automotive, electrical and household sectors.

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Features	Good Chemical Resistance Good Surface Finish High ESCR (Stress Crack Resist.) Low Shrinkage Low Warpage
Uses	Automotive Applications Electrical Housing Household Goods Housings
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.47	g/cm³	ASTM D792, ISO 1183
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg)	20.0	cm³/10min	ISO 1133
Molding Shrinkage
Flow : 3.18 mm	0.30	%
Across Flow	0.75	%	ISO 294-4
Flow	0.29	%	ISO 294-4
Water Absorption
Saturation	0.40	%	ASTM D570
Saturation, 23°C	0.40	%	ISO 62
Equilibrium, 50% RH	0.20	%	ASTM D570
Equilibrium, 23°C, 50% RH	0.20	%	ISO 62
Viscosity Number (Reduced Viscosity)	105.0	ml/g	ISO 1628

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	9700	MPa	ISO 527-2
Tensile Strength
Break, 23°C	125	MPa	ASTM D638, ISO 527-2
Break, -40°C	195	MPa	ISO 527-2
Break, 80°C	79.0	MPa	ISO 527-2
Break, 121°C	47.0	MPa	ISO 527-2
Tensile Elongation (Break, 23°C)	2.2	%	ASTM D638, ISO 527-2
Tensile Creep Modulus			ISO 899-1
1 hr	7600	MPa
1000 hr	6700	MPa
Flexural Modulus
23°C	8270	MPa	ASTM D790
23°C	8300	MPa	ISO 178
Flexural Strength (23°C)	194	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	9.0	kJ/m²	ISO 179
Charpy Unnotched Impact Strength			ISO 179
-30°C	50	kJ/m²
23°C	59	kJ/m²
Notched Izod Impact			ASTM D256
-40°C	69	J/m
23°C	85	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed	210	°C	ASTM D648, ISO 75-2/B
1.8 MPa, Unannealed	177	°C	ASTM D648
1.8 MPa, Unannealed	175	°C	ISO 75-2/A
Peak Melting Temperature	223	°C	ASTM D3418, ISO 3146
CLTE - Flow	4.0E-5	cm/cm/°C
RTI Elec			UL 746
0.690 mm	130	°C
1.50 mm	130	°C
3.00 mm	130	°C
RTI Imp			UL 746
0.690 mm	90.0	°C
1.50 mm	90.0	°C
3.00 mm	90.0	°C
RTI Str			UL 746
0.690 mm	130	°C
1.50 mm	130	°C
3.00 mm	130	°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity ¹	1.0E+14	ohms	ASTM D257, IEC 60093
Volume Resistivity
1.50 mm	> 1.0E+13	ohms·cm	ASTM D257
--	> 1.0E+13	ohms·cm	IEC 60093
Dielectric Constant			IEC 60250
100 Hz	3.80
1 MHz	3.70
Dissipation Factor			IEC 60250
100 Hz	3.0E-3
1 MHz	0.018
Comparative Tracking Index	500	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.690 mm	HB
1.50 mm	HB
3.00 mm	HB

Injection	Nominal Value	Unit
Drying Temperature	100 to 120	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.040	%
Processing (Melt) Temp	250 to 270	°C
Mold Temperature	60.0 to 100	°C
Injection Pressure	3.50 to 12.5	MPa
Injection Rate	Fast
Back Pressure	< 1.00	MPa

Note Message
1 .	1.5 mm

Resin Grade	Manufacturer	Category	Trademark
RTP 105	RTP Company	PP, Unspecified	RTP
Yuyao PBT 3066G20	Yuyao Tenglong Plastics Co., Ltd.	PBT	Yuyao PBT
ALKATEQ™ MD592UV	Marplex Australia Pty. Ltd.	MDPE	ALKATEQ™
Geon™ Vinyl Packaging 2710	PolyOne Corporation	PVC, Rigid	Geon™ Vinyl Packaging
LOXIM 840 02T HB	LOXIM Industries Private Limited	PP, Unspecified	LOXIM