ULTEM™ 9090 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0WuNBZ_ULTEM-9090-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyetherimide Blend with improved Ductility and Detergent resistance. Meets FAR 25.853 and OSU 55/55 heat release and provides low toxicity, smoke and flame evolution. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2900 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 95.0 | MPa | ASTM D638 |
| Yield | 97.0 | MPa | ISO 527-2/50 |
| Break 3 | 90.0 | MPa | ASTM D638 |
| Break | 80.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Break 5 | 85 | % | ASTM D638 |
| Break | 80 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3000 | MPa | ASTM D790 |
| -- 7 | 2800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 136 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D256 |
| -30°C 9 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 11 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Reverse Notch Izod Impact (3.20 mm) | 3300 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -20°C, Total Energy | 88.0 | J | |
| 0°C, Total Energy | 99.0 | J | |
| 23°C, Total Energy | 88.0 | J | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | 90 | % | |
| 0°C | 100 | % | |
| 23°C | 100 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| NBS Smoke Density - Flaming, Ds, 4 min | 0.700 | ASTM E662 | |
| OSU Peak Heat Release Rate 12 | 45.0 | kW/m² | FAR 25.853 |
| OSU Total Heat Release 13 | 15.0 | kW·min/m² | FAR 25.853 |
| Vertical Burn Test - Test a (60 s), passes at | 1.0 | sec | FAR 25.853 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 214 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 14 | 205 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 6.40 mm | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 15 | 190 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ISO 306/A50 |
| -- | 212 | °C | ISO 306/B50, ISO 306/B120 |
| CLTE | |||
| Flow : -20 to 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -20 to 150°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 46 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 330 to 390 | °C | |
| Middle Temperature | 335 to 390 | °C | |
| Front Temperature | 345 to 390 | °C | |
| Nozzle Temperature | 345 to 390 | °C | |
| Processing (Melt) Temp | 355 to 390 | °C | |
| Mold Temperature | 130 to 160 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 5 minute test |
| 13 . | 2 minute test |
| 14 . | 120*10*4 mm |
| 15 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEOPLAST 240 M/E | Zylog Plastalloys | TPE | NEOPLAST |
| Celstran® PA66-GF40-02P11 | Celanese Corporation | Nylon 66 | Celstran® |
| Colorite 77 Series 9077 | Colorite Polymers | PVC, Unspecified | Colorite 77 Series |
| Ecomass® 1700CO93 | Ecomass Technologies | Nylon 12 | Ecomass® |
| Kingfa HF-606 | Kingfa | ABS | Kingfa |