NORYL™ PX9406P resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zzgmnH_NORYLPX9406Presin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled NORYL CLASSICO grade for PV applications |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 260°C/10.0 kg | 13.0 | cm³/10min | ISO 1133 |
| 280°C/10.0 kg | 41.0 | cm³/10min | ISO 1133 |
| 280°C/5.0 kg | 13.0 | cm³/10min | ISO 1133 |
| 300°C/5.0 kg | 33.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2520 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 71.0 | MPa | ISO 527-2/50 |
| Fracture | 56.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.5 | % | ISO 527-2/50 |
| Fracture | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2520 | MPa | ISO 178 |
| Flexural Stress | 109 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/2U |
| Notched Izod Impact 2 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 117 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 140 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) | PLC 6 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 2.50 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (0.750 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 750 | °C | IEC 60695-2-13 |
| 1.50 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 X 58128 | RTP Company | Nylon 66 | RTP |
| SABIC® STAMAX 60YM240 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| LONGLITE® PBT 3020-104S | CCP Group | PBT | LONGLITE® PBT |
| Sylvin 9915-87 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ ATX3562R resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |