SABIC® HDPE CC2056
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zyaP68_SABICHDPECC2056.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE CC2056 is a high density polyethylene copolymer injection moulding grade. Its narrow molecular weight distribution and high flow results in low warpage, good rigidity, good gloss and fast moulding cycles. SABIC® HDPE CC2056 is typically used for caps and closures applications and thin wall articles. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (40°C, 1.00mm, 10% Igepal CO-630, compression molding) | 10.0 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(2.00 mm, Compression Molded) | 1200 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 2.00mm, molded | 28.0 | MPa | ASTM D638 |
| Fracture, 2.00mm, molded | 15.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 2.00 mm, Compression Molded) | > 200 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 3.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 128 | °C | ISO 306/A |
| Melting Temperature (DSC) | 132 | °C | ISO 11357-3 |
| Enthalpy Change | 210 | J/g | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec LD20-002 | Genesis Polymers | LDPE | SureSpec |
| Cariflex® IR0401 BU | Kraton Polymers LLC | IR | Cariflex® |
| Karina IVORY PVC COMPOUND -E 90850-35/1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® Frosted V045-68177 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| ULTEM™ HU2100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |