INELEC PPCF25
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INELEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zyWOzH_INELEC-PPCF25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% CARBON FIBER REINFORCED, ELECTRICALLY CONDUCTIVE POLYPROPYLENE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 38.6 | MPa | ASTM D638 |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact | 120 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 193 to 227 | °C | |
| Mold Temperature | 37.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E590PUOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Unilex™ UP.32.955A | United Polychem | HDPE | Unilex™ |
| Next Nylon 6 Prime Series NXIM-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Karina BLACK PVC COMPOUND E-CAK 60-48/1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® 7M | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |