GLS PP YT03
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zxGG6h_GLS-PP-YT03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 15 TALC PRECOLOR |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.990 to 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | > 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.1 to 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | > 2300 | MPa | ASTM D638 |
| Tensile Strength | > 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 9.0 | % | ASTM D638 |
| Flexural Modulus | > 1800 | MPa | ASTM D790 |
| Flexural Strength | > 44.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 58.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 235 | °C | |
| Mold Temperature | 33.0 to 65.0 | °C | |
| Injection Pressure | 70.0 to 104 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 30S5201 | The Matrixx Group, Inc. | PBT | Matrixx |
| Ultramid® 8202 HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| Chemraz 629 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Hanwha Total PE E153F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |
| LNP™ LUBRILOY™ Z20001 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRILOY™ |