ENGAGE™ 8130
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zuKGIG_ENGAGE-8130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8130 Polyolefin Elastomer is an ethylene-octene copolymer with low density and a high melt index. This combination provides excellent toughness, flexibility, and ease in processing and makes ENGAGE 8130 highly effective as an impact modifier in polyolefins or as a component in injection molding applications. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.864 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 4 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 63 | ||
| Shore D, 1 sec, Compression Molded | 13 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 1.80 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 2.40 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 7.80 | MPa | |
| 2% Secant : Compression Molded | 7.30 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 26.4 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -55.0 | °C | Internal Method |
| Melting Temperature (DSC) 5 | 56.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 38.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M864SE | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| TEKNIFLEX® COC P7P | Tekni-Films, a div of Tekni-Plex | Film, PP/COC/PP | TEKNIFLEX® |
| Dugdale PVC Flexible Injection Molding - Shore A 58 Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| Kingfa FRHIPS-702 | Kingfa | PS (HIPS) | Kingfa |
| KEBATRON® PPS L1040G3 | BARLOG plastics GmbH | PPS | KEBATRON® |