Plaslube® PA6/6 8111
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zuDU4b_Plaslube-PA6-6-8111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Advanced Aramid Lubrication package |
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.8 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 82.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 246 | °C | |
| 1.8 MPa, Unannealed | 146 | °C | |
| CLTE - Flow | 4.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66-MOS2 BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| AKROMID® A3 ICF 30 black (5021) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Evoprene™ 084 | AlphaGary | SBS | Evoprene™ |
| FHR Polypropylene P9M7R-056 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| LNP™ LUBRICOMP™ LX91475 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |