Hostacom HRC 242D NAT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zoLLpn_HostacomHRC242DNAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom HRC 242D NAT is a mineral filled PP homopolymer, with high melt flow rate. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.07 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 33.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2900 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 1.5 | kJ/m² | ISO 179/1eA |
| 23°C | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 0°C | 18 | kJ/m² | ISO 179/1eU |
| 23°C | 32 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 102 | °C | ISO 306/B |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT SG3181S | Sincerity Australia Pty Ltd. | PBT+PET | Sindustris PBT |
| AIE PET 40G8 | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| CONAPOXY® FR-1820 | Cytec Industries Inc. | Epoxy | CONAPOXY® |
| CP PRYME® Polypropylene PPH100-4M | Chase Plastics Services Inc. | PP Homopolymer | CP PRYME® Polypropylene |
| KOCETAL® K300 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |