LNP™ THERMOCOMP™ QC006 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zoG74U_LNP-THERMOCOMP-QC006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* QC006 is a compound based on Nylon 6/10 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound QC-1006 Product reorder name: QC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.20 | g/cm³ | |
| -- | 1.24 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 23000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 1 | 214 | MPa | ASTM D638 |
| Break | 243 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 2 | 3.0 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 3 | 16100 | MPa | ASTM D790 |
| -- 4 | 18800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 349 | MPa | ISO 178 |
| Yield, 50.0 mm Span 5 | 326 | MPa | ASTM D790 |
| Break, 50.0 mm Span 6 | 325 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 7 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 920 | J/m | ASTM D4812 |
| 23°C 8 | 59 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 4.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 221 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 211 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 213 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarGRIP GP 25-9000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarGRIP |
| TRENCHCOAT™ Protective Film | The Dow Chemical Company | Polyolefin, Unspecified | TRENCHCOAT™ |
| DeWAL DW 224 | DeWAL Industries | PTFE | DeWAL |
| ICORENE® 2551 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| INTOL® 1500 | Versalis S.p.A. | SBR, Emulsion | INTOL® |