Category: | PP, Unspecified , Polypropylene |
Manufacturer: | Putsch Kunststoffe GmbH |
Trademark: | FORMULA P |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | zoAOmp_FORMULA-P-FIB-3620-L-SC.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Polypropylene with 20% glass fiber reinforcement (chemically bonded). This material has very good stiffness and excellent heat resistance. |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.05 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
Molding Shrinkage | 0.25 - 0.35 | % | Internal method |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress | ISO 527-2 | ||
Yield | 75.0 | MPa | ISO 527-2 |
Fracture | 75.0 | MPa | ISO 527-2 |
Tensile Strain (Break) | 10 | % | ISO 527-2 |
Flexural Modulus | 4500 | MPa | ISO 178 |
Flexural Stress (3.5% Strain) | 90.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact | ISO 180 | ||
-20°C | 3.5 | kJ/m² | ISO 180 |
23°C | 5.5 | kJ/m² | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Vicat Softening Temperature | 125 | °C | ISO 306/B |
Additional Information |
---|
Tensile Strength, ISO 527: 75 MPa |
Injection | Nominal Value | Unit | |
---|---|---|---|
Processing (Melt) Temp | 220 - 260 | °C | |
Mold Temperature | 30.0 - 50.0 | °C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
MIDILENA III PPB200 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
DOW™ HDPE DMDA-8904 NT 7 | The Dow Chemical Company | HDPE | DOW™ HDPE |
AIE PPO 9010F-S100C | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
Kingfa API-1609 | Kingfa | PP, Unspecified | Kingfa |
MACOMASS PVC MM-PVC I 1595 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |