LEXAN™ FL2000 resin Datasheet,PC,SABIC Innovative Plastics-SHANGHAI SUSHENG

Message
LEXAN FL2000 is a medium flow specialty polycarbonate (PC) resin for structural foam molding, allowing for various weight reductions at 0.24" (6.0mm) wall. This product offers low temperature impact strength and high heat resistance in combination with LEXAN FL2000 resin is available in opaque colors only.

General Information
Features	Foamable property Medium liquidity Low temperature impact resistance Heat resistance, high
Appearance	Opacity
Processing Method	Foam treatment

Physical	Nominal Value	Unit	Test Method
Specific Gravity			ASTM D792
-- ¹	1.09	g/cm³	ASTM D792
--	1.21	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	10	g/10 min	ASTM D1238
Molding Shrinkage - Flow (6.40 mm)	0.60 - 0.80	%	Internal method
Water Absorption			ASTM D570
24 hr	0.13	%	ASTM D570
Equilibrium, 23°C	0.34	%	ASTM D570
Foam - Physical ²	10	%	Internal method

Mechanical	Nominal Value	Unit	Test Method
Foam - Mechanical ³	10	%	Internal method

Impact	Nominal Value	Unit	Test Method
Foam - Impact ⁴	10	%	Internal method

Thermal	Nominal Value	Unit	Test Method
Foam - Thermal ⁵	10	%	Internal method

Electrical	Nominal Value	Unit	Test Method
Foam - Electrical ⁶	20	%	Internal method

Flammability	Nominal Value	Unit	Test Method
Foam - Flame Class Minimum Density	940	kg/m³	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (6.40 mm)	2310	MPa	ASTM D638
Tensile Strength (Yield, 6.35 mm)	53.8	MPa	ASTM D638
Tensile Elongation (Break, 6.35 mm)	7.8	%	ASTM D638
Flexural Modulus (6.40 mm)	1930	MPa	ASTM D790
Flexural Strength (Yield, 6.40 mm)	75.8	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Unnotched Izod Impact (23°C, 6.40 mm)	2700	J/m	ASTM D4812
Instrumented Dart Impact			ASTM D3763
-40°C, Total Energy	8.13	J	ASTM D3763
-20°C, Total Energy	67.8	J	ASTM D3763
Dart Drop Impact (23°C)	122	J	Internal method

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, unannealed, 6.40mm	138	°C	ASTM D648
1.8 MPa, unannealed, 6.40mm	127	°C	ASTM D648
CLTE - Flow (-40 to 95°C)	5.6E-5	cm/cm/°C	ASTM E831
Specific Heat	1180	J/kg/°C	ASTM C351
RTI Elec	80.0	°C	UL 746
RTI Imp	80.0	°C	UL 746
RTI	80.0	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.1E+17	ohms	ASTM D257
Volume Resistivity	3.6E+16	ohms·cm	ASTM D257
Dielectric Constant			ASTM D150
100 Hz	2.47		ASTM D150
1 MHz	2.68		ASTM D150
Dissipation Factor			ASTM D150
100 Hz	3.7E-3		ASTM D150
1 MHz	3.9E-3		ASTM D150
Arc Resistance ⁷	PLC 6		ASTM D495
Comparative Tracking Index (CTI)	PLC 4		UL 746
High Amp Arc Ignition (HAI)	PLC 0		UL 746
High Voltage Arc Tracking Rate (HVTR)	PLC 3		UL 746
Hot-wire Ignition (HWI)	PLC 0		UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
3.91 mm	HB		UL 94
5.99 mm	V-1		UL 94
Oxygen Index	28	%	ASTM D2863

Additional Information
Structural Foam Molding - Blowing Agent, Chemical System: FLC298Structural Foam Molding - Blowing Agent, Physical System: Nitrogen GasStructural Foam Molding - Concentration Range (Blowing Agent): 3 - 5 %Structural Foam Molding - Drying Temperature (Blowing Agent): 104 °CStructural Foam Molding - Drying Temperature (Resin): 121 °CStructural Foam Molding - Drying Time (Blowing Agent): 4 hrsStructural Foam Molding - Drying Time (Resin): 3 - 4 hrsStructural Foam Molding - Drying Time (Resin, Cumulative): 48 hrsStructural Foam Molding - Front Temperature: 293 - 316 °CStructural Foam Molding - Melt Temperature: 291 - 310 °CStructural Foam Molding - Middle Temperature: 293 - 316 °CStructural Foam Molding - Mold Temperature: 71 - 93 °CStructural Foam Molding - Nozzle Temperature: 282 - 304 °CStructural Foam Molding - Rear Temperature: 238 - 260 °CStructural Foam Molding - Recommended Concentration (Blowing Agent): 1.5 %

Additional Information

Structural Foam Molding - Blowing Agent, Chemical System: FLC298Structural Foam Molding - Blowing Agent, Physical System: Nitrogen GasStructural Foam Molding - Concentration Range (Blowing Agent): 3 - 5 %Structural Foam Molding - Drying Temperature (Blowing Agent): 104 °CStructural Foam Molding - Drying Temperature (Resin): 121 °CStructural Foam Molding - Drying Time (Blowing Agent): 4 hrsStructural Foam Molding - Drying Time (Resin): 3 - 4 hrsStructural Foam Molding - Drying Time (Resin, Cumulative): 48 hrsStructural Foam Molding - Front Temperature: 293 - 316 °CStructural Foam Molding - Melt Temperature: 291 - 310 °CStructural Foam Molding - Middle Temperature: 293 - 316 °CStructural Foam Molding - Mold Temperature: 71 - 93 °CStructural Foam Molding - Nozzle Temperature: 282 - 304 °CStructural Foam Molding - Rear Temperature: 238 - 260 °CStructural Foam Molding - Recommended Concentration (Blowing Agent): 1.5 %

Note Message
1 .	Foam molded
2 .	6.4 mm wt reduction
3 .	6.4 mm wt reduction
4 .	6.4 mm wt reduction
5 .	6.4 mm wt reduction
6 .	6.4 mm wt reduction
7 .	Tungsten electrode

Category:	PC , Polycarbonate
Manufacturer:	SABIC Innovative Plastics
Trademark:	LEXAN™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zncNvk_LEXAN-FL2000-resin.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SEMICOSIL® 989/1K	Wacker Chemie AG	Silicone	SEMICOSIL®
SUPRENE® 5890F	SK Global Chemical	EPDM	SUPRENE®
Veroplas PA2001F	PlastxWorld Inc.	Nylon 6	Veroplas
Grilon® TSG-50	EMS-GRIVORY	Nylon 66/6	Grilon®
Itenite® 817	ITEN INDUSTRIES	TPV	Itenite®