Plaslube® Actrn
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zmPzXu_Plaslube-Actrn.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This acetal (homopolymer) is lubricated with a binary polymer lubricant blend. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 2.5 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2480 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 82.7 | MPa | ASTM D790 |
| Compressive Strength | 68.9 | MPa | ASTM D695 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.14 | ASTM D1894 | |
| With steel-static | 0.10 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| CLTE - Flow | 9.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Thrust Washer Wear Factor, ASTM D3702, 2000 PV, ambient temp.: 40E-10in³min/ft-lb-hrThrust Washer Wear Factor, ASTM D3702, 12000 PV, 300°F: 10E-10in³min/ft-lb-hrJournal Bearing Wear Factor, 5000 PV, ambient temp.: 35E-10in³min/ft-lb-hrCoefficient of Friction, Static, Thrust washer, 40psi, ambient temp.: 0.10Coefficient of Friction, Dynamic, Thrust washer, 40psi, 50 ft/min, ambient temp.: 0.14Limiting PV, Thrust washer, 100 FPM, ambient temp.: 4E4e |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 177 - 193 | °C | |
| Middle Temperature | 188 - 210 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 177 - 204 | °C | |
| Processing (Melt) Temp | 193 - 216 | °C | |
| Mold Temperature | 82.2 - 121 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 70 - 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-IM4 | Polymer Resources Ltd. | PC | PRL |
| RAMLLOY PB917G6 | Polyram Ram-On Industries | Nylon 6+PP | RAMLLOY |
| Unichem 1116G-015 | Colorite Polymers | PVC, Flexible | Unichem |
| Andur 9000 AS/Curative | Anderson Development Company | PUR-TDI | Andur |
| POLYFLAM® RABS 90950 UV5 | A. Schulman Europe | ABS | POLYFLAM® |