Epoxies, Ect. 20-2180

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Epoxies, Etc.
Trademark:	Epoxies, Ect.
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zka86R_Epoxies-Ect-20-2180.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

This series of polyurethane systems is engineered for electronic potting, encapsulating, and casting applications. They are low in viscosity, low in toxicity and available in the popular TriggerBond® dual barrel cartridge dispensing system. These elastomeric systems are suitable for a variety of electronic insulating applications. The durometers range from an enterable gel to Shore A 80.

Green:

The base Natural Oil Polyol (NOP) used in these systems is obtained directly from a plant source without chemical modifications. Using renewable resources, such as NOP's, will reduce the demand on non-renewable fossil fuels and reduce the overall production of carbon dioxide.

Features:

Green

Low Viscosity

Available in TriggerBond®

Low Durometer

Moisture Resistant

Convenient Mix Ratios

Low Shrinkage & Exotherm

Benefits

Reduce demand on non-renewable fossil fuels

Quick self leveling around components

Easy to use packaging

Low stress on components & vibration resistant

Can be used in wet environments

Easy to process by hand or with meter mix

Less stress to components during cure

General Information
Features	Electrically Insulating Low Exotherm Low Shrinkage Low to No Water Absorption Low Toxicity Low Viscosity Renewable Resource Content
Uses	Electrical/Electronic Applications
Appearance	Black
Processing Method	Casting Encapsulating Potting

Thermal	Nominal Value	Unit
CLTE - Flow	2.1E-4	cm/cm/°C
Thermal Conductivity	0.30	W/m/K

Electrical	Nominal Value	Unit
Surface Resistivity	> 1.0E+15	ohms

Thermoset	Nominal Value	Unit
Thermoset Mix Viscosity (25°C)	1700	cP

Additional Information	Nominal Value	Unit
Operating Temperature	-30.0 to 125	°C

Uncured Properties	Nominal Value	Unit
Color	Black
Mix Ratio by Weight (PBW)
Part A	100
Part B	60
Mix Ratio by Volume (PBV)
Part A	2.0
Part B	1.0
Density
25°C ¹	0.968	g/cm³
25°C ²	1.15	g/cm³
Viscosity
25°C ³	1.5	Pa·s
25°C ⁴	2.2	Pa·s
Curing Time
85°C	0.66	hr
65°C	1.5	hr
45°C	2.5	hr
25°C	24	hr
Gel Time (25°C)	20	min

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	80
Tensile Strength	11.7	MPa
Tensile Elongation at Break	220	%
Tear Strength	14.0	kN/m
Electric Strength	26	kV/mm
Relative Permittivity (1 kHz)	3.40
Volume Resistivity	7.2E+14	ohms·cm
Dissipation Factor (1 kHz)	0.017

Note Message
1 .	Part B
2 .	Part A
3 .	Part A
4 .	Part B

Resin Grade	Manufacturer	Category	Trademark
Trovidur® W 2000	Röchling Engineering Plastics SE & Co. KG	PVC, Flexible	Trovidur®
Nipol® LX844C	Zeon Corporation	Latex	Nipol®
Alathon® M4621	LyondellBasell Industries	HDPE Copolymer	Alathon®
Chemlon® 243 GU	Teknor Apex Company (Chem Polymer)	Nylon 6	Chemlon®
NORYL™ SE1GFN3 resin	SABIC Innovative Plastics	PPE+PS	NORYL™