CALIBRE™ 303V-6
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zkEurv_CALIBRE-303V-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 303V-6 Polycarbonate resin offers exceptional impact resistance and heat distortion resistance, and meets UL94 V-2 rating. CALIBRE 303V-6 contains a mold release agent, a UV stabilizer additive, and is available in opaque white color only. Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(2.00 mm) | 2410 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 72.4 | MPa | |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Break 4 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2 |
| Flexural Modulus 5 | 2410 | MPa | ASTM D790 |
| Flexural Strength 6 | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 910 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 | |
| Instrumented Dart Impact (23°C, Total) | 90.4 | J | ASTM D3763 |
| Tensile Impact Strength | 588 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 142 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 122 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 139 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 |
| CLTE - Flow (-40 to 82°C) | 5.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 7 | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Oxygen Index 8 | 26 | % | ISO 4589-2 |
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 51 mm/min |
| 5 . | Type I, 1.3 mm/min |
| 6 . | Type I, 1.3 mm/min |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V876 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TAISOX 7350F | Formosa Plastics Corporation | EVA | TAISOX |
| Ultramid® 8233G HS | BASF Corporation | Nylon 6 | Ultramid® |
| Starpylen HW 30K ECR | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| Sylvin 9067-95LMW Grey 9368 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |