Braskem PE LL6901S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zg4Qev_Braskem-PE-LL6901S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LL6901S is a LLDPE Butene copolymer produced by Braskem. It is a ready to use product since it's been compounded with 15% LDPE. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel contained. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.68 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 40.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 30.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 930 | % | |
| TD : Break, 38 µm, Blown Film | 1200 | % | |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 38 µm, Blown Film | 160 | MPa | |
| 1% Secant, TD : 38 µm, Blown Film | 170 | MPa | |
| Dart Drop Impact (38 µm, Blown Film) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Blown Film | 60 | g | |
| TD : 38 µm, Blown Film | 520 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm, Blown Film) | 127 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 302 | RTP Company | PC | RTP |
| Softell TBP 237D NAT | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
| LG PVC LP170G | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| PERLER® N09V3000B01 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |
| Sylvin 7868-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |