TAROMID B 240
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zfN78e_TAROMID-B-240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 low viscosity. Available: all colors also dry blend (DB), UV stabilized (L), heat stabilized (H), fast cycles (S) and lubricated (W). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 to 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/1.0 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 to 1.6 | % | |
| Across Flow | 1.1 to 1.6 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 2.0 | % | ASTM D570, ISO 62 |
| Saturation | 9.0 | % | ASTM D570 |
| Saturation, 23°C | 9.0 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2850 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 70.0 | MPa | |
| Break | 62.0 | MPa | |
| Tensile Elongation (Break) | 100 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2750 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Yield | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 3.0 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 40 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 74.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 2 | 80.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ASTM D1525, ISO 306/A50 4 3 |
| -- | 200 | °C | ASTM D1525, ISO 306/B50 5 4 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 220 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 to 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 18 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-2 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 23 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 20000 hrs |
| 3 . | Rate A (50°C/h), Loading 1 (10 N) |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 203 H | RTP Company | Nylon 66 | RTP |
| Shandong Nylon A4TR04 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| TEREZ PC 9005 SZ | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| Karina BLACK PVC COMPOUND -E 851-48/ 1-F-ISM (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 120 01 V0 | LOXIM Industries Private Limited | PC | LOXIM |