Ixef® BM-1524
| Category: | PARA , Polyarylamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ixef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zec6dv_IxefBM1524.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ixef 1524 is a 50% glass fiber reinforced, halogen-free flame retardant polyacrylamide with high strength, high rigidity, good surface gloss and excellent creep resistance. -black: Ixef 1524/9008 -customers can color by themselves |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Water Absorption (Balanced, 65% RH) | 0.28 | % | ISO 62 |
| Mold shrinkage- Flow | 0.10 - 0.30 | % | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vertical combustion-60 seconds (8.89cm) 1 | 5.0 | sec | DMS 1510 |
| Toxic gas emission | BSS 7239/ATS 1000/ABD 0031 | ||
| CO | 100 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| HCL | ppm | BSS 7239/ATS 1000/ABD 0031 | |
| HCN | 15 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| HF | ppm | BSS 7239/ATS 1000/ABD 0031 | |
| NO + NO2 | ppm | BSS 7239/ATS 1000/ABD 0031 | |
| SO2 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20000 | MPa | ISO 527-2 |
| Tensile Strength (Yield) | 248 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 19300 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 376 | MPa | ASTM D790 |
| Compressive Modulus | 16500 | MPa | ASTM D695 |
| Compressive Strength | 328 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 227 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant 2(2.40 GHz) | 4.44 | ASTM D2520 | |
| Dissipation Factor 3(2.40 GHz) | 0.012 | ASTM D2520 | |
| Comparative Tracking Index (CTI) (3.00 mm) | > 600 | V | UL 746 |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.400 mm | 37.6 | UL 746 | |
| 0.750 mm | 53.6 | UL 746 | |
| 1.50 mm | 70.2 | UL 746 | |
| 3.00 mm | 95.4 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.40 mm | PLC 2 | UL 746 | |
| 0.75 mm | PLC 2 | UL 746 | |
| 1.5 mm | PLC 1 | UL 746 | |
| 3.0 mm | PLC 1 | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) (3.00 mm) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.400 mm | 95 | sec | UL 746 |
| 0.750 mm | > 120 | sec | UL 746 |
| 1.50 mm | > 120 | sec | UL 746 |
| 3.00 mm | > 120 | sec | UL 746 |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.40 mm | PLC 1 | UL 746 | |
| 0.75 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 4(0.40 mm, ALL) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.40 mm | 775 | °C | IEC 60695-2-13 |
| 0.75 mm | 800 | °C | IEC 60695-2-13 |
| 1.5 mm | 825 | °C | IEC 60695-2-13 |
| 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 37 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 1.0 - 3.0 | hr | |
| Rear Temperature | 250 - 260 | °C | |
| Front Temperature | 260 - 290 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Injection instructions |
|---|
| 热流道系统：250 °C～260 °C （ 482°F～500 °F ） 射出压力：快速 干燥： 该树脂应该干燥～要求的0.10% 含湿率。 如果使用的除湿空气干燥机露点为-28 ° C（ -18 °F ）或更低，应遵循以下规则：120 ° C（248 °F）温度下 1〜2小时， 100℃ C（ 212°F）温度下2〜4小时，或80 ℃（176 °F）温度下2-8小时。 注塑成型： IXEF1524混合物在大多数螺杆注塑机上均可以很容易地注射成型。建议采用通用螺杆，背压尽可能低。 测得的熔融温度应该在270℃ （518° F）左右，机筒后端温度应该在250～260℃ （ 482～500°F ）左右，前端逐渐增至260 ℃〜275℃ （500～527 °F）。如果使用热流道，温度应设置为250～260 ℃（482～500 ° F ） 。 为了最大限度地提高结晶度，模腔表面温度必须保持在120～140℃（ 248～284°F）之间。成型温度低，容易使产品产生翘曲、外观不良，并极可能产生蠕变。射出压力应确保快速射出。调整保压压力和时间，尽量提高零件的重量。部件正好完全填充完毕（ 95-99％）前，将注塑件从射出部位转移到螺杆位置进行保压。 |
| Note Message | |
|---|---|
| 1 . | DMS 1510/14 CFR 25.853 Appendix F Part 1, (a), 1, (i) |
| 2 . | Method B |
| 3 . | Method B |
| 4 . | These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ P70A-22U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| BMC 620 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| HiFill® POM HO 0167 S1 | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Hostacom CR 250 F C21451 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| OTECH PVC PL1001-11 - Riser Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |